Fracture Origins in Miniature Silicon Carbide Structures

George D. Quinn; William N. Sharpe; Glenn M. Beheim; Noel N. Nemeth; Osama Jadaan

doi:10.4028/www.scientific.net/KEM.290.62

Fracture Origins in Miniature Silicon Carbide Structures

George D. Quinn, William N. Sharpe, Glenn M. Beheim, Noel N. Nemeth, Osama Jadaan

Research output: Contribution to journal › Article › peer-review

Original language	American English
Journal	Key Engineering Materials
Volume	290
DOIs	https://doi.org/10.4028/www.scientific.net/KEM.290.62
State	Published - Jul 1 2005
Externally published	Yes

Disciplines

Metallurgy
Materials Science and Engineering

Access to Document

10.4028/www.scientific.net/KEM.290.62License: Unspecified

Cite this

@article{45980ce6bd9c4f0a88135489019fbf76,

title = "Fracture Origins in Miniature Silicon Carbide Structures",

author = "Quinn, {George D.} and Sharpe, {William N.} and Beheim, {Glenn M.} and Nemeth, {Noel N.} and Osama Jadaan",

note = "Direct tension strength tests were conducted on chemical vapor deposited silicon carbide microspecimens. Three types of specimens were used: straight gage section, tapered gage section, and notched gage section. The average strengths and standards deviations were: 0.42 GPa ± 0.13 GPa; 0.47 GPa ± 0.16 GPa; and 0.68 GPa ± 0.19 GPa, respectively.",

year = "2005",

month = jul,

day = "1",

doi = "10.4028/www.scientific.net/KEM.290.62",

language = "American English",

volume = "290",

journal = "Key Engineering Materials",

issn = "1013-9826",

}

TY - JOUR

T1 - Fracture Origins in Miniature Silicon Carbide Structures

AU - Quinn, George D.

AU - Sharpe, William N.

AU - Beheim, Glenn M.

AU - Nemeth, Noel N.

AU - Jadaan, Osama

N1 - Direct tension strength tests were conducted on chemical vapor deposited silicon carbide microspecimens. Three types of specimens were used: straight gage section, tapered gage section, and notched gage section. The average strengths and standards deviations were: 0.42 GPa ± 0.13 GPa; 0.47 GPa ± 0.16 GPa; and 0.68 GPa ± 0.19 GPa, respectively.

PY - 2005/7/1

Y1 - 2005/7/1

UR - https://www.scientific.net/KEM.290.62

U2 - 10.4028/www.scientific.net/KEM.290.62

DO - 10.4028/www.scientific.net/KEM.290.62

M3 - Article

SN - 1013-9826

VL - 290

JO - Key Engineering Materials

JF - Key Engineering Materials

ER -

Fracture Origins in Miniature Silicon Carbide Structures

Disciplines

Access to Document

Other files and links

Cite this